[산업] 바커케미칼 액상 실리콘 고무 (Liquid Silicone Rubber), LSR
|
제품명 |
기술 자료 |
제품특성 |
|||||
|
|
Appearance |
Hardness Shore A |
Tensile strength |
Elongation at break |
Tear strength |
Compression Set |
Specific Features |
|
slightly bluish |
30[1] |
8.6 N/mm²[2] |
860 %[3] |
32 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
40[1] |
9.0 N/mm²[2] |
580 %[3] |
38 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
50[1] |
9.1 N/mm²[2] |
490 %[3] |
54 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
60[1] |
9.0 N/mm²[2] |
380 %[3] |
50 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
70[1] |
9.5 N/mm²[2] |
370 %[3] |
36 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
dark-gray / black |
55[1] |
6.3 N/mm²[2] |
300 %[3] |
15 N/mm[4] |
13 %[5] |
Flame retardant, Reduced volatile content |
|
|
colourless |
33[1] |
7.0 N/mm²[2] |
460 %[3] |
29 N/mm[4] |
11 %[5] |
Low viscosity, Reduced volatile content |
|
|
transparent |
3[1] |
1.3 N/mm²[2] |
700 %[3] |
3 N/mm[4] |
16 %[5] |
General purpose, Reduced volatile content |
|
|
transparent |
6[1] |
2.8 N/mm²[2] |
700 %[3] |
7 N/mm[4] |
16 %[5] |
General purpose, Reduced volatile content |
|
|
transparent |
12[1] |
4.2 N/mm²[2] |
760 %[3] |
13 N/mm[4] |
13 %[5] |
General purpose, Reduced volatile content |
|
|
transparent |
22[1] |
8.3 N/mm²[2] |
870 %[3] |
24 N/mm[4] |
17 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
30[1] |
7.0 N/mm²[2] |
610 %[3] |
21 N/mm[4] |
10 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
30[1] |
7.5 N/mm²[2] |
600 %[3] |
20 N/mm[4] |
10 %[5] |
Food-contact, Reduced volatile content |
|
|
transparent |
40[1] |
10.0 N/mm²[2] |
610 %[3] |
30 N/mm[4] |
11 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
50[1] |
10.3 N/mm²[2] |
490 %[3] |
26 N/mm[4] |
13 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
60[1] |
9.8 N/mm²[2] |
340 %[3] |
27 N/mm[4] |
16 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
70[1] |
9.3 N/mm²[2] |
290 %[3] |
20 N/mm[4] |
16 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
77[1] |
8.3 N/mm²[2] |
240 %[3] |
12 N/mm[4] |
17 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
85[1] |
6.5 N/mm²[2] |
130 %[3] |
11 N/mm[4] |
14 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
90[1] |
7.0 N/mm²[2] |
50 %[3] |
8 N/mm[4] |
16 %[5] |
Food-contact, General purpose, Reduced volatile content |
|
|
transparent |
30[1] |
7.1 N/mm²[2] |
620 %[3] |
24 N/mm[4] |
10 %[5] |
Fast curing, Food-contact, Reduced volatile content |
|
|
transparent |
40[1] |
9.2 N/mm²[2] |
610 %[3] |
29 N/mm[4] |
10 %[5] |
Fast curing, Food-contact, Reduced volatile content |
|
|
transparent |
50[1] |
10.0 N/mm²[2] |
480 %[3] |
27 N/mm[4] |
15 %[5] |
Fast curing, Food-contact, Reduced volatile content |
|
|
transparent |
60[1] |
9.6 N/mm²[2] |
380 %[3] |
25 N/mm[4] |
18 %[5] |
Fast curing, Food-contact, Reduced volatile content |
|
|
transparent |
70[1] |
9.9 N/mm²[2] |
310 %[3] |
20 N/mm[4] |
11 %[5] |
Fast curing, Food-contact, Reduced volatile content |
|
|
transparent |
30[1] |
6.0 N/mm²[2] |
610 %[3] |
16 N/mm[4] |
13 %[6] |
Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
transparent |
40[1] |
7.8 N/mm²[2] |
600 %[3] |
22 N/mm[4] |
16 %[6] |
Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
transparent |
50[1] |
8.7 N/mm²[2] |
500 %[3] |
24 N/mm[4] |
15 %[6] |
Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
transparent |
60[1] |
9.5 N/mm²[2] |
380 %[3] |
28 N/mm[4] |
15 %[6] |
Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
transparent |
70[1] |
8.5 N/mm²[2] |
330 %[3] |
23 N/mm[4] |
19 %[6] |
Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
dark-gray / black |
50[1] |
10.0 N/mm²[2] |
510 %[3] |
28 N/mm[4] |
13 %[5] |
Flame retardant, Reduced volatile content |
|
|
beige |
50[1] |
5.4 N/mm²[2] |
470 %[3] |
12 N/mm[4] |
18 %[6] |
Oil resistant, Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
beige |
70[1] |
6.1 N/mm²[2] |
280 %[3] |
15 N/mm[4] |
16 %[6] |
Oil resistant, Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
white-off |
65[1] |
8.7 N/mm²[2] |
350 %[3] |
26 N/mm[4] |
15 %[6] |
Oil resistant, Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
60[1] |
6.1 N/mm²[2] |
280 %[3] |
13 N/mm[4] |
10 %[5] |
Steam resistant, Food-contact, Reduced volatile content, Hot water resistant |
|
|
opaque |
61[1] |
6.1 N/mm²[2] |
270 %[3] |
14 N/mm[4] |
7 %[5] |
Ultra-low compression set, Reduced volatile content, Coolant resistant |
|
|
opaque |
60[1] |
5.9 N/mm²[2] |
300 %[3] |
15 N/mm[4] |
11 %[6] |
Low compression set without post-cure, Reduced volatile content, Coolant resistant |
|
|
transparent |
40[1] |
7.0 N/mm²[2] |
500 %[3] |
31 N/mm[4] |
11 %[6] |
Fast curing, Low compression set without post-cure |
|
|
transparent |
30[1] |
9.8 N/mm²[2] |
740 %[3] |
35 N/mm[4] |
14 %[5] |
Fast curing, Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
40[1] |
9.0 N/mm²[2] |
600 %[3] |
36 N/mm[4] |
11 %[5] |
Fast curing, Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
50[1] |
9.2 N/mm²[2] |
500 %[3] |
40 N/mm[4] |
11 %[5] |
Fast curing, Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
60[1] |
9.4 N/mm²[2] |
380 %[3] |
38 N/mm[4] |
15 %[5] |
Fast curing, Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
70[1] |
8.0 N/mm²[2] |
370 %[3] |
40 N/mm[4] |
15 %[5] |
Fast curing, Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
40[1] |
9.8 N/mm²[2] |
660 %[3] |
36 N/mm[4] |
25 %[5] |
Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
50[1] |
9.4 N/mm²[2] |
460 %[3] |
46 N/mm[4] |
25 %[5] |
Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
60[1] |
9.2 N/mm²[2] |
390 %[3] |
47 N/mm[4] |
20 %[5] |
Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
70[1] |
9.5 N/mm²[2] |
280 %[3] |
21 N/mm[4] |
22 %[5] |
Food-contact, High tear-resistant, Reduced volatile content |
|
|
transparent |
30[1] |
7.5 N/mm²[2] |
650 %[3] |
24 N/mm[4] |
17 %[6] |
Low compression set without post-cure, Low coefficient of friction, Reduced volatile content |
|
|
transparent |
50[1] |
9.0 N/mm²[2] |
460 %[3] |
31 N/mm[4] |
15 %[6] |
Low compression set without post-cure, Low coefficient of friction, Reduced volatile content |
|
|
transparent |
30[1] |
7.8 N/mm²[2] |
660 %[3] |
31 N/mm[4] |
12 %[5] |
Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
40[1] |
9.3 N/mm²[2] |
580 %[3] |
32 N/mm[4] |
12 %[5] |
Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
50[1] |
8.9 N/mm²[2] |
440 %[3] |
31 N/mm[4] |
16 %[5] |
Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
60[1] |
9.3 N/mm²[2] |
330 %[3] |
24 N/mm[4] |
19 %[5] |
Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
70[1] |
8.3 N/mm²[2] |
270 %[3] |
18 N/mm[4] |
17 %[5] |
Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
77[1] |
6.9 N/mm²[2] |
180 %[3] |
11 N/mm[4] |
13 %[5] |
Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
20[1] |
6.6 N/mm²[2] |
820 %[3] |
15 N/mm[4] |
43 %[7] |
Self-adhesive |
|
|
transparent |
30[1] |
7.7 N/mm²[2] |
730 %[3] |
18 N/mm[4] |
38 %[7] |
Self-adhesive |
|
|
transparent |
40[1] |
8.7 N/mm²[2] |
670 %[3] |
24 N/mm[4] |
37 %[7] |
Self-adhesive |
|
|
transparent |
50[1] |
9.2 N/mm²[2] |
490 %[3] |
20 N/mm[4] |
22 %[7] |
Self-adhesive |
|
|
transparent |
60[1] |
9.1 N/mm²[2] |
460 %[3] |
23 N/mm[4] |
21 %[7] |
Self-adhesive |
|
|
transparent |
30[1] |
7.9 N/mm²[2] |
780 %[3] |
20 N/mm[4] |
40 %[7] |
Self-adhesive, Food-contact, Reduced volatile content |
|
|
transparent |
40[1] |
8.5 N/mm²[2] |
660 %[3] |
21 N/mm[4] |
40 %[7] |
Self-adhesive, Food-contact, Reduced volatile content |
|
|
transparent |
50[1] |
8.2 N/mm²[2] |
560 %[3] |
25 N/mm[4] |
50 %[7] |
Self-adhesive, Food-contact, Reduced volatile content |
|
|
transparent |
50[1] |
10.0 N/mm²[2] |
560 %[3] |
28 N/mm[4] |
51 %[7] |
Self-adhesive, Food-contact, Reduced volatile content |
|
|
transparent |
60[1] |
9.1 N/mm²[2] |
520 %[3] |
27 N/mm[4] |
53 %[7] |
Self-adhesive, Food-contact, Reduced volatile content |
|
|
opaque |
30[1] |
7.4 N/mm²[2] |
710 %[3] |
17 N/mm[4] |
27 %[7] |
Self-adhesive, Oil bleeding |
|
|
opaque |
40[1] |
8.8 N/mm²[2] |
620 %[3] |
21 N/mm[4] |
21 %[7] |
Self-adhesive, Oil bleeding |
|
|
opaque |
50[1] |
8.6 N/mm²[2] |
510 %[3] |
23 N/mm[4] |
12 %[7] |
Self-adhesive, Oil bleeding |
|
|
opaque |
60[1] |
6.8 N/mm²[2] |
360 %[3] |
14 N/mm[4] |
15 %[7] |
Self-adhesive, Coolant resistant |
|
|
transparent |
20[1] |
5.3 N/mm²[2] |
680 %[3] |
13 N/mm[4] |
17 %[7] |
Self-adhesive |
|
|
transparent |
30[1] |
4.9 N/mm²[2] |
620 %[3] |
12 N/mm[4] |
13 %[7] |
Self-adhesive |
|
|
transparent |
40[1] |
8.5 N/mm²[2] |
590 %[3] |
24 N/mm[4] |
11 %[7] |
Self-adhesive |
|
|
- |
50[1] |
8.7 N/mm²[2] |
490 %[3] |
23 N/mm[4] |
9 %[7] |
Self-adhesive |
|
|
transparent |
60[1] |
8.2 N/mm²[2] |
430 %[3] |
30 N/mm[4] |
12 %[7] |
Self-adhesive |
|
|
transparent |
70[1] |
7.7 N/mm²[2] |
350 %[3] |
25 N/mm[4] |
10 %[7] |
Self-adhesive |
|
|
black |
66[1] |
10.0 N/mm²[2] |
330 %[3] |
25 N/mm[4] |
10 %[5] |
Heat resistant, Reduced volatile content, Low compression set |
|
|
black |
63[1] |
8.5 N/mm²[2] |
330 %[3] |
24 N/mm[4] |
7 %[5] |
Ultra-low compression set, Heat resistant, Reduced volatile content |
|
|
black |
60[1] |
10.0 N/mm²[2] |
400 %[3] |
28 N/mm[4] |
18 %[6] |
Heat resistant, Fast curing, Low compression set without post-cure, Reduced volatile content |
|
|
colorless |
60[1] |
7.5 N/mm²[2] |
170 %[3] |
14 N/mm[4] |
- |
Fast curing |
|
|
black |
54[1] |
5.6 N/mm²[2] |
340 %[3] |
14 N/mm[4] |
- |
Electrically conductive, Reduced volatile content |
|
|
dark-gray / black |
45[1] |
9.2 N/mm²[2] |
590 %[3] |
23 N/mm[4] |
34 %[7] |
Flame retardant, Self-adhesive, Reduced volatile content |
|
|
transparent |
45[1] |
6.3 N/mm²[2] |
540 %[3] |
34 N/mm[4] |
45 %[7] |
Self-adhesive, Food-contact, Reduced volatile content, Hot water resistant |
|
|
white |
50[1] |
7.8 N/mm²[2] |
450 %[3] |
26 N/mm[4] |
- |
X-ray opaque, Food-contact, Reduced volatile content |
|
|
transparent |
30[1] |
8.9 N/mm²[2] |
770 %[3] |
29 N/mm[4] |
33 %[7] |
Self-adhesive, Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
40[1] |
8.8 N/mm²[2] |
680 %[3] |
25 N/mm[4] |
30 %[7] |
Self-adhesive, Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
transparent |
50[1] |
8.2 N/mm²[2] |
610 %[3] |
28 N/mm[4] |
61 %[6] |
Self-adhesive, Food-contact, Low coefficient of friction, Reduced volatile content, Less self-healing |
|
|
opaque |
50[1] |
9.0 N/mm²[2] |
490 %[3] |
30 N/mm[4] |
13 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
40[1] |
8.0 N/mm²[2] |
610 %[3] |
25 N/mm[4] |
13 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
50[1] |
8.5 N/mm²[2] |
460 %[3] |
37 N/mm[4] |
12 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
60[1] |
9.2 N/mm²[2] |
420 %[3] |
38 N/mm[4] |
13 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
68[1] |
8.5 N/mm²[2] |
380 %[3] |
28 N/mm[4] |
16 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
30[1] |
8.0 N/mm²[2] |
680 %[3] |
22 N/mm[4] |
16 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
30[1] |
7.2 N/mm²[2] |
700 %[3] |
22 N/mm[4] |
17 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
42[1] |
8.5 N/mm²[2] |
580 %[3] |
24 N/mm[4] |
15 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
50[1] |
8.5 N/mm²[2] |
500 %[3] |
36 N/mm[4] |
14 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
21[1] |
6.1 N/mm²[2] |
800 %[3] |
16 N/mm[4] |
16 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
30[1] |
7.0 N/mm²[2] |
750 %[3] |
19 N/mm[4] |
15 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
21[1] |
6.2 N/mm²[2] |
850 %[3] |
16 N/mm[4] |
18 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
opaque |
32[1] |
6.5 N/mm²[2] |
650 %[3] |
22 N/mm[4] |
14 %[6] |
Fast curing, Oil bleeding, Low compression set without post-cure, Reduced volatile content |
|
|
slightly bluish |
30[1] |
8.6 N/mm²[2] |
860 %[3] |
32 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
40[1] |
9.0 N/mm²[2] |
580 %[3] |
38 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
45[1] |
9.0 N/mm²[2] |
580 %[3] |
41 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
50[1] |
9.1 N/mm²[2] |
490 %[3] |
54 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
60[1] |
9.0 N/mm²[2] |
380 %[3] |
50 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
slightly bluish |
70[1] |
9.5 N/mm²[2] |
370 %[3] |
36 N/mm[4] |
- |
Fast curing, Low volatile, Food-contact, High tear-resistant |
|
|
ivory |
36[1] |
5.4 N/mm²[2] |
500 %[3] |
11 N/mm[4] |
- |
- |
|
|
white |
40[1] |
2.8 N/mm²[2] |
210 %[3] |
4.6 N/mm[4] |
- |
- |
|
|
transparent |
30[1] |
1.7 N/mm²[2] |
290 %[3] |
4.9 N/mm[4] |
- |
- |
|
|
transparent |
36[1] |
5.0 N/mm²[2] |
350 %[3] |
10 N/mm[4] |
- |
- |
|
|
ivory |
39[1] |
5.1 N/mm²[2] |
380 %[3] |
8.9 N/mm[4] |
- |
- |
|
|
transparent |
20[1] |
2.4 N/mm²[2] |
450 %[3] |
4.3 N/mm[4] |
- |
- |
|
|
transparent |
60[1] |
5.0 N/mm²[2] |
150 %[3] |
6.1 N/mm[4] |
- |
- |
|
[산업] 바커케미칼 상온경화형 일액형과 이액형 실리콘 고무(RTV-...
[건축] MS폴리머 기반 접착제 Flex 310 M® ProSeal : 분체 도장, ...
-
[산업] 알파 DP007 하이브리드 실란트 접착제
-
[산업] 초고온 실리콘 실란트 -40°F(-40°C) ~ 1000°F(538°C) : Seal & Assist 5000
-
[전기/전자] 다우코닝 DOWSIL RTV-3145 접착 실란트/투명,회색 제품
-
[건축] 아크릴 테코레이터 코크(ACRYLIC DECORATORS CAULK) - AC 38
-
[산업/식품] Seal &Bond MS24ICE 접착제 - 영하에서도 경화되는 접착제, 식품인증
-
[산업] 버사켐 메가 블랙 실리콘 (mega grey silicone) 가스켓 : (-73~343°C)
-
[산업] 버사켐 메가 그레이 실리콘 (mega grey silicone) 가스켓 : (-54~343°C)
-
[산업] 바커케미칼 상온경화형 일액형과 이액형 실리콘 고무(RTV-1 / RTV-2)
-
[산업] 바커케미칼 액상 실리콘 고무 (Liquid Silicone Rubber), LSR
-
[건축] MS폴리머 기반 접착제 Flex 310 M® ProSeal : 분체 도장, 아연 도금, 양극 산화 처리, 크롬 처리, 용융 아연 도금 표면 접착
-
[산업] 세메다인 수퍼엑스 시리즈(Super X series) 접착제 - 케미칼별 내화학성과 인장접착강도
-
[산업] 세메다인 수퍼엑스 시리즈(Super X series) 접착제 - 고무 피착제 인장접착강도
-
[산업] 세메다인 수퍼엑스 시리즈(Super X series) 접착제 - 피착제별 인장접착강도
-
[산업] 모멘티브 비초산 속경화형 TSE-397 : MIL-A-46146B
-
[전자] 다우 전기전자용 실리콘 접착제 제품 리스트 전자부품 조립용
-
[전자] 플랙시블 실리콘 접착제 DOWSIL™ VE-8001
-
[건축] 다우실(DOWSIL™ ) 732 다용도 실란트
-
[건축/산업] 바커 ELASTOSIL® 실리콘 실란트 제품 리스트
-
[건축] 폴리우레아 속경화형 실란트 HSC-S600P/R : 크랙보수, 줄눈처리, 조인트 실링, 폐수 및 수처리 시설
-
[건축] 1액형 수팽창 우레탄 씰란트 VAROSEAL HS-450WS : 건축, 토목공사의 각종 조인트 지수, 시공이음부, 관통부의 둘레 지수