[산업] 웨이콘 모델, 주형 및 템플릿의 주조, 다공성 및 손상된 주조의 수리, 프로토 타입: Plastic Metal F2

Base

알루미늄 분말과 에폭시 수지

Specific Properties

viscous

Colour after curing

aluminium

Mixing ratio by weight resin/hardener

100:14

Density of the mixture (200g preparation)

1,45 g/cm³

Viscosity of the mixture

200.000 mPa·s

Consumption at a coating thickness of 1,0 mm

1,45 kg/m²

Maximium layer thickness for each working step

10 mm

Pot life at +20°C (+68°F) 200g preparation

60 min

Curing time mechanical loads

16 h

Final hardness after

24 h

Mean strength at +25°C (+77°F) acc. to DIN EN 1465/ASTM D 1002:

Pressure

43 Mpa

Pull

14 Mpa

Bending

26 Mpa

E-Modul

1.500 - 2.000 Mpa

Shore hardness D (ATSM D 1706)

79

Shrinkage

0,025 %

Tg after curing at room temperature

51,5 °C

Tg after tempering (at 120 °C)

53,1 °C

Thermoforming resistance

(-31°F) -35 to (+248°F) +120 °C

Resistivity

7,36 · 10^12 Ωm

Thermal diffusivity (23 °C)

0,737 mm²/s

Thermal conductivity

0,98 W/m·K

Specific heat capacity

0,824 J/(g·K)

ISSA-Code

75.509.11/12

IMPA-Code

812933/34