Base | 알루미늄 분말과 에폭시 수지 |
Specific Properties | viscous |
Colour after curing | aluminium |
Mixing ratio by weight resin/hardener | 100:14 |
Density of the mixture (200g preparation) | 1,45 g/cm³ |
Viscosity of the mixture | 200.000 mPa·s |
Consumption at a coating thickness of 1,0 mm | 1,45 kg/m² |
Maximium layer thickness for each working step | 10 mm |
Pot life at +20°C (+68°F) 200g preparation | 60 min |
Curing time mechanical loads | 16 h |
Final hardness after | 24 h |
Mean strength at +25°C (+77°F) acc. to DIN EN 1465/ASTM D 1002: | |
Pressure | 43 Mpa |
Pull | 14 Mpa |
Bending | 26 Mpa |
E-Modul | 1.500 - 2.000 Mpa |
Shore hardness D (ATSM D 1706) | 79 |
Shrinkage | 0,025 % |
Tg after curing at room temperature | 51,5 °C |
Tg after tempering (at 120 °C) | 53,1 °C |
Thermoforming resistance | (-31°F) -35 to (+248°F) +120 °C |
Resistivity | 7,36 · 10^12 Ωm |
Thermal diffusivity (23 °C) | 0,737 mm²/s |
Thermal conductivity | 0,98 W/m·K |
Specific heat capacity | 0,824 J/(g·K) |
ISSA-Code | 75.509.11/12 |
IMPA-Code | 812933/34 |
- 웨이콘,
- 모델,
- 주형,
- 템플릿의 주조,
- 다공성및 손상된 주조의 수리,
- 프로토 타입,
- Plastic Metal F2,
번호 | 제목 | 글쓴이 | 날짜 | 조회 수 |
---|---|---|---|---|
» | [산업] 웨이콘 모델, 주형 및 템플릿의 주조, 다공성 및 손상된 주조의 수리, 프로토 타입: Plastic Metal F2 | 아리랑 | 2021.03.30 | 461 |
5 | [산업] Ultra 1500 BD : 접착 씰란트, 고온용 조립품, 제작, 제조, 접착, 보수, 조립, 밀봉 | 아리랑 | 2022.08.11 | 187 |
4 | [산업] 웨이콘 (weicon) 보수용 알루미늄 퍼티 | 아리랑 | 2022.11.26 | 112 |
3 | [산업] 금속보수제 대체 비교표 (EGK, 데브콘(DEVCON), 벨조나(BELZONA) | 아리랑 | 2023.04.06 | 34 |
2 | [산업] 버사켐 [Versachem] 헤비듀티 테일파이트 보수 키트 | 아리랑 | 2023.03.20 | 13 |
1 | [산업] 수처리시설(상하수도) - 친환경 고분자. 세라믹 복합 방수 코팅제(CS-970) | 아리랑 | 2023.05.05 | 8 |